While there exists a number of materials to choose from while deploying polymer solution casting technology, the material science work continues in the areas of wall thickness, strength, lubricity, biocompatibility and clarity as well as interactions of the liquid polymers with extruded and injection molded components.
Alternately, resin casting may be accomplished with a resin plus a nearly equal amount of a "hardener" liquid (as in many epoxy resin or polyester resin systems), which functionally contains a second polymer, for use in forming a final product plastic which is a copolymer. Copolymers contain two different alternating chemical entities in the ...
In solvent casting and particulate leaching (SCPL), a polymer is dissolved in an organic solvent. Particles, mainly salts, with specific dimensions are then added to the solution. The mixture is shaped into its final geometry. For example, it can be cast onto a glass plate to produce a membrane or in a three-dimensional mold to produce a scaffold.
Casting is a manufacturing process in which a liquid material is usually poured into a mold, which contains a hollow cavity of the desired shape, and then allowed to solidify. The solidified part is also known as a casting, which is ejected or broken out of the mold to complete the process.
Synthetic casting "resin" for embedding display objects in Plexiglas/Lucite is simply methyl methacrylate liquid, into which a polymerization catalyst is added and mixed, causing it to "set" (polymerize). The polymerization creates a block of PMMA plastic ("acrylic glass") which holds the display object inside a transparent block.
Liquid-crystal polymers are present in melted/liquid or solid form. [7] In solid form, the main example of lyotropic LCPs is the commercial aramid known as Kevlar . The chemical structure of this aramid consists of linearly substituted aromatic rings linked by amide groups.
Plastisol. A plastisol is a colloidal dispersion of small polymer particles, usually polyvinyl chloride (PVC), in a liquid plasticizer.When heated to around 180 °C (356 °F), the plastic particles absorb the plasticizer, causing them to swell and fuse together forming a viscous gel.
Plastic sprue. In injection molding, sprue refers to the passage through which a liquid material (such as polystyrene or polyvinyl chloride) flows into a die, where the material solidifies to form parts. Sprue also refers to the material that solidifies in these passages, forming a framework that attaches the parts in a roughly planar arrangement.