The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [ 7 ] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa ) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3). ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M.
The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels.
The properties of steel depend on its microstructure: the arrangement of different phases, some harder, some with greater ductility. At the atomic level, the four phases of auto steel include martensite (the hardest yet most brittle), bainite (less hard), ferrite (more ductile), and austenite (the most ductile). The phases are arranged by ...
Characteristics – Generally consisting of portland cement, water, construction aggregate (coarse and fine), and steel reinforcing bars , concrete is cheaper in comparison to structural steel. Strength – Concrete is a composite material with relatively high compressive strength properties, but lacking in tensile strength/ductility. This ...