Fatigue has traditionally been associated with the failure of metal components which led to the term metal fatigue. In the nineteenth century, the sudden failing of metal railway axles was thought to be caused by the metal crystallising because of the brittle appearance of the fracture surface, but this has since been disproved. [ 1 ]
The fatigue limit or endurance limit is the stress level below which an infinite number of loading cycles can be applied to a material without causing fatigue failure. [1] Some metals such as ferrous alloys and titanium alloys have a distinct limit, [ 2 ] whereas others such as aluminium and copper do not and will eventually fail even from ...
Rainflow counting identifies the closed cycles in a stress-strain curve. The rainflow-counting algorithm is used in calculating the fatigue life of a component in order to convert a loading sequence of varying stress into a set of constant amplitude stress reversals with equivalent fatigue damage.
Various vibration-fatigue methods estimate damage intensity based on moments of the PSD, which characterize the statistical properties of the random process. The formulas for calculating such estimate are empirical (with very few exceptions) and are based on numerous simulations of random processes with known PSD. As a consequence, the accuracy ...
Modern procedures for critical plane analysis trace back to research published in 1973 in which M. W. Brown and K. J. Miller observed that fatigue life under multiaxial conditions is governed by the experience of the plane receiving the most damage, and that both tension and shear loads on the critical plane must be considered.
Low cycle fatigue (LCF) has two fundamental characteristics: plastic deformation in each cycle; and low cycle phenomenon, in which the materials have finite endurance for this type of load. The term cycle refers to repeated applications of stress that lead to eventual fatigue and failure; low-cycle pertains to a long period between applications.
Strength parameters include: yield strength, tensile strength, fatigue strength, crack resistance, and other parameters. [citation needed] Yield strength is the lowest stress that produces a permanent deformation in a material.
Material failure theory is an interdisciplinary field of materials science and solid mechanics which attempts to predict the conditions under which solid materials fail under the action of external loads.