Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an electrochemical process in which one metal corrodes preferentially when it is in electrical contact with another, in the presence of an electrolyte.
Galvanic corrosion of an aluminium plate occurred when the plate was connected to a mild steel structural support.. Galvanic corrosion occurs when two different metals have physical or electrical contact with each other and are immersed in a common electrolyte, or when the same metal is exposed to electrolyte with different concentrations.
A galvanic anode, or sacrificial anode, is the main component of a galvanic cathodic protection system used to protect buried or submerged metal structures from corrosion. They are made from a metal alloy with a more "active" voltage (more negative reduction potential / more positive oxidation potential ) than the metal of the structure.
Corrosion of iron nail with coiled copper in medium with ferroxyl indicator. Ferroxyl indicator, or rust indicator, is a solution containing potassium hexacyanoferrate(III), phenolphthalein and sodium chloride. It turns blue in the presence of Fe 2+ ions, and pink in the presence of hydroxide (OH −) ions.
Over time the galvanic anode continues to corrode, consuming the anode material until eventually it must be replaced. Galvanic or sacrificial anodes are made in various shapes and sizes using alloys of zinc, magnesium, and aluminum. ASTM International publishes standards on the composition and manufacturing of galvanic anodes. [10] [11] [12]
The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the difference in ...
The corrosion is identifiable by presence of patches of brown-red powder deposit on the exposed copper. [ 1 ] Red plague is caused by normally occurring electrode potential difference between the copper and silver, leading to galvanic corrosion occurring in pits or breaks in the silver plating.
These zones also act as local galvanic couples, causing local galvanic corrosion. This condition happens when the material is heated to temperatures around 700 °C for too long a time, and often occurs during welding or an improper heat treatment. When zones of such material form due to welding, the resulting corrosion is termed weld decay.