Ductile iron is used in many piano harps (the iron plates which anchor piano strings). Ductile iron is used for vises. Previously, regular cast iron or steel was commonly used. The properties of ductile iron make it a significant upgrade in strength and durability from cast iron without having to use steel, which is expensive and has poor ...
Developed in 1948, nodular or ductile cast iron has its graphite in the form of very tiny nodules with the graphite in the form of concentric layers forming the nodules. As a result, the properties of ductile cast iron are that of a spongy steel without the stress concentration effects that flakes of graphite would produce.
Austempered Ductile Iron (ADI) is a form of ductile iron that enjoys high strength and ductility as a result of its microstructure controlled through heat treatment. While conventional ductile iron was discovered in 1943 and the austempering process had been around since the 1930s, the combination of the two technologies was not commercialized ...
There are many such savings possible in the specific case of converting a quench-and-tempered steel component to austempered ductile iron (ADI). Ductile iron is 10% less dense than steel and can be cast near to net shape, both characteristics that reduce the casting weight. Near-net-shape casting also further reduces the machining cost, which ...
Ductile iron pipe is pipe made of ductile cast iron commonly used for potable water transmission and distribution. [1] This type of pipe is a direct development of earlier cast iron pipe , which it has superseded.
The local necking and the cup and cone fracture surfaces are typical for ductile metals. This tensile test of a nodular cast iron demonstrates low ductility. Ductility refers to the ability of a material to sustain significant plastic deformation before fracture. Plastic deformation is the permanent distortion of a material under applied stress ...
Cast iron is a brittle form of iron which is weaker in tension than in compression. It has a relatively low melting point, good fluidity, castability, excellent machinability and wear resistance. Though almost entirely replaced by steel in building structures, cast irons have become an engineering material with a wide range of applications ...
The ductile to brittle transition temperature is lower than many other ductile iron alloys. In order to properly form the spherical-shaped nodules of graphite (called temper graphite nodules or temper carbon nodules) in the annealing process, care must be taken to ensure that the iron casting will solidify with an entirely white iron cross section.