In most of the world, sheet metal thickness is consistently specified in millimeters. In the U.S., the thickness of sheet metal is commonly specified by a traditional, non-linear measure known as its gauge. The larger the gauge number, the thinner the metal. Commonly used steel sheet metal ranges from 30 gauge to about 7 gauge.
Corrugated iron in the Cobar Sound Chapel, used both for the roof and as the formwork for the concrete interior. Typical corrugated galvanised iron appearance, with visible large flake type patterns. The galvanised sheet is viewed from below and is supported by a piece of angle iron (painted white). Corrugated galvanised iron (CGI) or steel ...
Phosphate conversion coating. Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1][2][3] It is one of the most common types of conversion ...
Structural steel. Structural steel is a category of steel used for making construction materials in a variety of shapes. Many structural steel shapes take the form of an elongated beam having a profile of a specific cross section. Structural steel shapes, sizes, chemical composition, mechanical properties such as strengths, storage practices ...
Hot-dip galvanization. Hot-dip galvanization is a form of galvanization. It is the process of coating iron and steel with zinc, which alloys with the surface of the base metal when immersing the metal in a bath of molten zinc at a temperature of around 450 °C (842 °F). When exposed to the atmosphere, the pure zinc (Zn) reacts with oxygen (O 2 ...
Galvannealed. Galvannealed or galvanneal (galvannealed steel) is the result from the processes of galvanizing followed by annealing of sheet steel. Galvannealed steel is a matte uniform grey color, which can be easily painted. In comparison to galvanized steel the coating is harder, and more brittle.
Cold-formed steel, especially in the form of thin gauge sheets, is commonly used in the construction industry for structural or non-structural items such as columns, beams, joists, studs, floor decking, built-up sections and other components. Such uses have become more and more popular in the US since their standardization in 1946.
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.