Polymer stabilizers (British English: polymer stabilisers) are chemical additives which may be added to polymeric materials to inhibit or retard their degradation. Mainly they protect plastic and rubber products against heat, oxidation, and UV light.
Antiozonants prevents or retards the degradation of polymers caused by ozone (ozone cracking) sequestrants, forming chelate complexes and inactivating traces of metal ions that would otherwise act as catalysts; ultraviolet stabilizers are used to protect polymers from effects of ultraviolet radiation and come to 2 main types.
Hindered amine light stabilizers (HALS) are chemical compounds containing an amine functional group that are used as stabilizers in plastics and polymers. [1] These compounds are typically derivatives of tetramethylpiperidine and are primarily used to protect the polymers from the effects of photo-oxidation; as opposed to other forms of polymer degradation such as ozonolysis.
In materials science, a thermosetting polymer, often called a thermoset, is a polymer that is obtained by irreversibly hardening ("curing") a soft solid or viscous liquid prepolymer . [1] Curing is induced by heat or suitable radiation and may be promoted by high pressure or mixing with a catalyst .
The onset of thermal degradation dictates the maximum temperature at which a polymer can be used. It is an important limitation in how the polymer is manufactured and processed. For instance, polymers become less viscous at higher temperatures which makes injection moulding easier and faster, but thermal degradation places a ceiling temperature ...
A thermoset polymer matrix is a synthetic polymer reinforcement where polymers act as binder or matrix to secure in place incorporated particulates, fibres or other reinforcements. They were first developed for structural applications, [ 1 ] such as glass-reinforced plastic radar domes on aircraft and graphite - epoxy payload bay doors on the ...
Polymers become charged through the dissociation of the monomer side groups. If more monomer side groups are dissociated, the polymer has a higher charge. In turn, the charge of the polymer classifies the polyelectrolyte, which can be positive (cationic) or negative (anionic).
Polymerization in which polymer is formed in monomer, or monomer-solvent droplets in a continuous phase that is a nonsolvent for both the monomer and the formed polymer. Note 1: In suspension polymerization, the initiator is located mainly in the monomer phase. Note 2: Monomer or monomer-solvent droplets in suspension polymerization have