T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10]
T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
Alloys with higher copper content (alloyings 6061, 6056, 6013) are mainly used in aviation. ... Tensile strength/MPa Elongation at break/% Brinell hardness
By comparison, annealed type 316 stainless steel has a density of 8000 kg/m 3, modulus of 193 GPa, and tensile strength of 570 MPa. [23] Tempered 6061 aluminium alloy has a density of 2700 kg/m 3, modulus of 69 GPa, and tensile strength of 310 MPa, respectively. [24] Ti-6Al-4V standard specifications include: [25] [26]
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
This Thanksgiving is expected to be the busiest ever for air travel, with a record-setting 18 million Americans expected to jet off for their holiday celebrations in the coming days.
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061.The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.