Concrete tests can measure the "plastic" (unhydrated) properties of concrete prior to, and during placement. As these properties affect the hardened compressive strength and durability of concrete (resistance to freeze-thaw), the properties of workability (slump/flow), temperature, density and age are monitored to ensure the production and ...
Concrete has a total embodied energy of 1.69 GJ/tonne, lower per unit mass than most common building materials besides wood. However, concrete structures often have high masses, so this comparison is not always directly relevant to decision making. Additionally, this value is based only on mix proportions of up to 20% fly ash.
Example of flat piece of concrete having dislodged with corroded rebar underneath, Welland River bridge across Queen Elizabeth Way in Niagara Falls, Ontario. The expansion of the corrosion products (iron oxides) of carbon steel reinforcement structures may induce internal mechanical stress (tensile stress) that cause the formation of cracks and disrupt the concrete structure.
Concrete has a very low coefficient of thermal expansion and shrinks as it matures. All concrete structures crack to some extent, due to shrinkage and tension. Concrete that is subjected to long-duration forces is prone to creep. Tests can be performed to ensure that the properties of concrete correspond to specifications for the application.
Concrete spalling from the ceiling of an office unit (interior) in Singapore, possibly due to rebar corrosion. Reinforced concrete can fail due to inadequate strength, leading to mechanical failure, or due to a reduction in its durability. Corrosion and freeze/thaw cycles may damage poorly designed or constructed reinforced concrete.
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
The adhesive properties of polymer concrete allow repair of both polymer and conventional cement-based concretes. The corrosion resistance and low permeability of polymer concrete allows it to be used in swimming pools, sewer structure applications, drainage channels, electrolytic cells for base metal recovery, and other structures that contain ...
For shrinkage, however, the weight loss of the drying test specimens must also be measured (or else the problem of updating is ill-conditioned). A fully rational prediction of concrete creep and shrinkage properties from its composition is a formidable problem, far from resolved satisfactorily.