The Electrochemical Fatigue Crack Sensor. In 1992, Dr. Campbell Laird and Dr. Yuanfeng Li invented the EFS™. The EFS™ relies on a patented electrical test [2] [3] method, which monitors the current flow at the surface of a metal while it is being mechanically flexed. The output current resembles a heart’s EKG pattern and can be ...
Fatigue has traditionally been associated with the failure of metal components which led to the term metal fatigue. In the nineteenth century, the sudden failing of metal railway axles was thought to be caused by the metal crystallising because of the brittle appearance of the fracture surface, but this has since been disproved. [ 1 ]
Scanning electron microscope image of fatigue striations produced from constant amplitude loading. The crack is growing from left to right. Striations are marks produced on the fracture surface that show the incremental growth of a fatigue crack. A striation marks the position of the crack tip at the time it was made.
In true corrosion fatigue, the fatigue-crack-growth rate is enhanced by corrosion; this effect is seen in all three regions of the fatigue-crack growth-rate diagram. The diagram on the left is a schematic of crack-growth rate under true corrosion fatigue; the curve shifts to a lower stress-intensity-factor range in the corrosive environment.
Dye penetrant inspection (DP), also called liquid penetrate inspection (LPI) or penetrant testing (PT), is a widely applied and low-cost inspection method used to check surface-breaking defects in all non-porous materials (metals, plastics, or ceramics).
White etching cracks (WEC), or white structure flaking or brittle flaking, is a type of rolling contact fatigue (RCF) damage that can occur in bearing steels under certain conditions, such as hydrogen embrittlement, high stress, inadequate lubrication, and high temperature. WEC is characterised by the presence of white areas of microstructural ...
Cracks that would normally have been invisible are detectable due to the magnetic particles clustering at the crack openings. The scale at the bottom is numbered in centimetres. Magnetic particle inspection ( MPI ) is a nondestructive testing process where a magnetic field is used for detecting surface, and shallow subsurface, discontinuities ...
The stress intensity factor at the crack tip of a compact tension specimen is [4] = [() / / + / / + /] where is the applied load, is the thickness of the specimen, is the crack length, and is the effective width of the specimen being the distance between the centreline of the holes and the backface of the coupon.