Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
#4 Dairy or sanitary finish. This finish is commonly used for the medical and food industry and almost exclusively used on stainless steel. This finish is much finer than a #4 architectural finish. This finish enhances the physical appearance of the metal as well as increases the sanitary benefits. [6]
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
Available finishes are #2B, #3, and #4. Grade 303 is not available in sheet form. [5] Grade 316 possesses more corrosion resistance and strength at elevated temperatures than 304. It is commonly used for pumps, valves, chemical equipment, and marine applications. Available finishes are #2B, #3, and #4. [5]
Mill finish is the surface texture (or finish) of metal after it exits a rolling mill, extrusion die, or drawing processes, including sheet, bar, plate, or structural shapes. This texture is usually rough and lacks lustre; it may have spots of oxidation or contamination with mill oil.
Brushed stainless steel or dull polished metal [1] is metal with a unidirectional satin finish. It is produced by polishing the metal with a 120–180 grit belt or wheel then softening with an 80–120 grit greaseless compound or a medium non-woven abrasive belt or pad. Commonly brushed metals include stainless steel, aluminium and nickel.
Type 310 310S— is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the steel excellent oxidation resistance as well as high strength at high temperature. This grade is also very ductile, and has good weldability enabling its widespread usage in many applications. [7]
In addition to the descriptive steel grade naming system indicated above, within EN 10027-2 is defined a system for creating unique steel grade numbers. While less descriptive and intuitive than the grand names they are easier to tabulate and use in data processing applications.