Type 310 310S— is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the steel excellent oxidation resistance as well as high strength at high temperature. This grade is also very ductile, and has good weldability enabling its widespread usage in many applications. [7]
UNS K11547 is T2 tool steel; UNS S17400 is ASTM grade 630, Cr-Ni 17-4PH precipitation hardened stainless steel; UNS S30400 is SAE 304, Cr/Ni 18/10, Euronorm 1.4301 stainless steel; UNS S31600 is SAE 316; UNS S31603 is 316L, a low carbon version of 316. The digits "03" were assigned since the maximum allowed carbon content is 0.03%; UNS C90300 ...
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
Comparison of steel grades by chemistry [4] [5] [6] EN steel number (Europe) EN steel name (Europe) ASTM grade (USA) AISI/SAE grade (USA) UNS (USA) DIN (Germany) BS (UK) UNI (Italy) JIS (Japan) Carbon steels 1.1141 1.0401 1.0453: C15D C18D: 1010 1018: CK15 C15 C16.8: 040A15 080M15 080A15 EN3B: C15 C16 1C15: S12C S15 S15CK S15C 1.0503 1.1191 1. ...
corrosion-resistant [steel] Largely synonymous with stainless steel, unless specific grades, specs, and distinctions are made on the drawing. Some people treat CRES as a subset of the stainless steels. CRS: cold rolled steel; on centres: Defines centre-to-centre distance of two features, such as two holes. C/T Correlation / Tracking C'BORE or ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
A #4 architectural finish is characterized by fine polishing grit lines that are uniform and directional in appearance. It is produced by polishing the metal with a 120–180 grit belt or wheel finish and then softened with an 80–120 grit greaseless compound or a medium non woven abrasive belt or pad. #4 Dairy or sanitary finish