Typical lectromechanical Universal Testing Machine Test fixture for three point flex test. A universal testing machine (UTM), also known as a universal tester, [1] universal tensile machine, materials testing machine, materials test frame, is used to test the tensile strength (pulling) and compressive strength (pushing), flexural strength, bending, shear, hardness, and torsion testing ...
Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
The four-point flexural test provides values for the modulus of elasticity in bending, flexural stress, flexural strain and the flexural stress-strain response of the material. This test is very similar to the three-point bending flexural test. The major difference being that with the addition of a fourth bearing the portion of the beam between ...
Rockwell hardness test (HR), principally used in the USA; Shore durometer hardness, used for polymers; Barcol hardness test, for composite materials; Tensile testing, used to obtain the stress-strain curve for a material, and from there, properties such as Young modulus, yield (or proof) stress, tensile stress and % elongation to failure ...
The test method for conducting the test usually involves a specified test fixture on a universal testing machine. Details of the test preparation, conditioning, and conduct affect the test results. The sample is placed on two supporting pins a set distance apart. Calculation of the flexural stress
During the testing for determination of the loads, no fracture must occur at the ultimate load for a period of 3 seconds. This is also commonly used in knowing the properties of metal beams. For example, it is used in experiments such as T.T.M. (tensile testing machine) and U.T.M. (universal testing machine)
It is a generalized form of tensile testing in which the material sample is simultaneously stressed along two perpendicular axes. Typical materials tested in biaxial configuration include metal sheets, [1] silicone elastomers, [2] composites, [3] thin films, [4] textiles [5] and biological soft tissues. [6] An example of a biaxial tensile machine.
Also acid ionization constant or acidity constant. A quantitative measure of the strength of an acid in solution expressed as an equilibrium constant for a chemical dissociation reaction in the context of acid-base reactions. It is often given as its base-10 cologarithm, p K a. acid–base extraction A chemical reaction in which chemical species are separated from other acids and bases. acid ...