The Liberty Head nickel, sometimes referred to as the V nickel because of its reverse (or tails) design, is an American five-cent piece. It was struck for circulation from 1883 until 1912, with at least five pieces being surreptitiously struck dated 1913. The obverse features a left-facing image of the goddess of Liberty.
Electroless nickel immersion gold (ENIG or ENi/IAu), also known as immersion gold (Au), chemical Ni/Au or soft gold, is a metal plating process used in the manufacture of printed circuit boards (PCBs), to avoid oxidation and improve the solderability of copper contacts and plated through-holes.
Gold plated - gold layer thickness greater than or equal to 0.5 micron; Heavy gold plated / Vermeil - gold layer thickness greater than or equal to 2.5 micron; Gold plated silver jewellery can still tarnish as the silver atoms diffuse into the gold layer, causing slow gradual fading of its color and eventually causing tarnishing of the surface ...
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...
Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used. [1]
Electroless nickel plating, covered by a thin layer of gold, is used in the manufacture of printed circuit boards (PCBs), to avoid oxidation and improving the solderability of copper contacts and plated through holes and vias. The gold is typically applied by quick immersion in a solution containing gold salts.
A nickel's melt value fell below its face value from late 2008 through mid-2010, and more recently again from late mid-2012. [114] In February 2014, it was reported that the Mint was conducting experiments to use copper-plated zinc (the same composition used for the United States 1 cent coin) for the nickel. [115]
The design of the American Buffalo gold bullion coin is a modified version of James Earle Fraser's design for the Indian Head nickel (Type 1), issued in early 1913. After a raised mound of dirt below the animal on the reverse was reduced, the Type 2 variation continued to be minted for the rest of 1913 and every year until 1938, except for 1922, 1932, and 1933 when no nickels were struck.