Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
Schematic and dimensions of a compact tension specimen. A compact tension specimen (CT) is a type of standard notched specimen in accordance with ASTM [1] and ISO [2] standards. Compact tension specimens are used extensively in the area of fracture mechanics and corrosion testing, in order to establish fracture toughness and fatigue crack ...
The dimensions of the testing material must maintain proportionality. The specimen is placed on the work table and a notch is created exactly at the centre. The crack should be generated such that the defect length is about half the depth. The load applied on the specimen is generally a three-point bending load.
The type of notch introduced to a specimen depends on the material and characterization employed. For standardized testing of fracture toughness by the Charpy impact method, specimen and notch dimensions are most often taken from American standard ASTM E23, or British standard BS EN ISO 148-1:2009.
ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M. Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation ) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%.
In practice this is not always feasible, since even in tensile tests, certain properties can be influenced by specimen size and/or geometry. Here is a listing of some of the most common tests: [2] Hardness Testing. Vickers hardness test (HV), which has one of the widest scales; Brinell hardness test (HB)
1940s flexural test machinery working on a sample of concrete Test fixture on universal testing machine for three-point flex test. The three-point bending flexural test provides values for the modulus of elasticity in bending, flexural stress, flexural strain and the flexural stress–strain response of the material.
The Los Angeles abrasion test (LA abrasion) is the North American standard for testing toughness (resistance to abrasion and degradation [1]) of construction aggregate or gravel and its suitability for road construction. Test methodology and equipment is defined in the ASTM International publications ASTM C131 for particle sizes smaller than 37 ...