Mu-metal has several compositions. One such composition is approximately 77% nickel, 16% iron, 5% copper, and 2% chromium or molybdenum. [1] [2]More recently, mu-metal is considered to be ASTM A753 Alloy 4 and is composed of approximately
Carbonyl iron has lower losses than hydrogen-reduced iron, but also lower permeability. A popular application of carbonyl iron-based magnetic cores is in high-frequency and broadband inductors and transformers, especially higher power ones. Carbonyl iron cores are often called "RF cores".
They also have high magnetic permeability. These so-called ceramic magnets are cheap, and are widely used in household products such as refrigerator magnets . The maximum magnetic field B is about 0.35 tesla and the magnetic field strength H is about 30–160 kiloampere turns per meter (400–2000 oersteds ). [ 33 ]
The most common soft ferrites are: Manganese-zinc ferrite (MnZn, with the formula Mn a Zn (1−a) Fe 2 O 4). MnZn have higher permeability and saturation levels than NiZn. Nickel-zinc ferrite (NiZn, with the formula Ni a Zn (1−a) Fe 2 O 4). NiZn ferrites exhibit higher resistivity than MnZn, and are therefore more suitable for frequencies ...
Magnetically hard materials have high coercivity, whereas magnetically soft materials have low coercivity. The overall strength of a magnet is measured by its magnetic moment or, alternatively, its total magnetic flux. The local strength of magnetism in a material is measured by its magnetization.
Below 912 °C (1,674 °F), iron has a body-centered cubic (bcc) crystal structure and is known as α-iron or ferrite. It is thermodynamically stable and a fairly soft metal. α-Fe can be subjected to pressures up to ca. 15 GPa before transforming into a high-pressure form termed ε-Fe discussed below.
Get answers to your AOL Mail, login, Desktop Gold, AOL app, password and subscription questions. Find the support options to contact customer care by email, chat, or phone number.
Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000) [ clarification needed ] , low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T [ clarification needed ] .