Example Bjerrum plot: Change in carbonate system of seawater from ocean acidification.. A Bjerrum plot (named after Niels Bjerrum), sometimes also known as a Sillén diagram (after Lars Gunnar Sillén), or a Hägg diagram (after Gunnar Hägg) [1] is a graph of the concentrations of the different species of a polyprotic acid in a solution, as a function of pH, [2] when the solution is at ...
Carbonatation is a slow process that occurs in concrete where lime (CaO, or Ca(OH) 2 ) in the cement reacts with carbon dioxide (CO 2) from the air and forms calcium carbonate. The water in the pores of Portland cement concrete is normally alkaline with a pH in the range of 12.5 to 13.5.
Calcium hydroxide is modestly soluble in water, as seen for many dihydroxides. Its solubility increases from 0.66 g/L at 100 °C to 1.89 g/L at 0 °C. [8] Its solubility product K sp of 5.02 × 10 −6 at 25 °C, [1] its dissociation in water is large enough that its solutions are basic according to the following dissolution reaction:
An example is when slaked lime (calcium hydroxide) is mixed into a thick slurry with sand and water to form mortar for building purposes. When the masonry has been laid, the slaked lime in the mortar slowly begins to react with carbon dioxide to form calcium carbonate (limestone) according to the reaction: Ca(OH) 2 + CO 2 → CaCO 3 + H 2 O.
The following chart shows the solubility of various ionic compounds in water at 1 atm pressure and room temperature (approx. 25 °C, 298.15 K). "Soluble" means the ionic compound doesn't precipitate, while "slightly soluble" and "insoluble" mean that a solid will precipitate; "slightly soluble" compounds like calcium sulfate may require heat to precipitate.
Calcium looping (CaL), or the regenerative calcium cycle (RCC), is a second-generation carbon capture technology. [1] It is the most developed form of carbonate looping, where a metal (M) is reversibly reacted between its carbonate form (MCO 3) and its oxide form (MO) to separate carbon dioxide from other gases coming from either power generation or an industrial plant.
Ca(OH) 2 or CaO · H 2 O: Calcium hydroxide (portlandite) C-S-H: 0.6–2.0 CaO · SiO 2 · 0.9–2.5 H 2 O, with variable composition within this range, and often also incorporating partial substitution of Al for Si: Calcium silicate hydrate: C-A-H: Phase more complex than C-S-H: Calcium aluminate hydrate C-A-S-H: This is even more complex than ...
The alkali–carbonate reaction is an alteration process first suspected in the 1950s in Canada for the degradation of concrete containing dolomite aggregates. [1] [2]Alkali from the cement might react with the dolomite crystals present in the aggregate inducing the production of brucite, (MgOH) 2, and calcite (CaCO 3).