The flow table test or slump-flow test is a method to determine consistency of fresh concrete. Flow table test is also used to identify transportable moisture limit of solid bulk cargoes. [ 1 ] It is used primarily for assessing concrete that is too fluid (workable) to be measured using the slump test , because the concrete will not retain its ...
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
The test is carried out using a metal mould in the shape of a conical frustum known as a slump cone or Abrams cone, that is open at both ends and has attached handles.The tool typically has an internal diameter of 100 millimetres (3.9 in) at the top and of 200 millimetres (7.9 in) at the bottom with a height of 305 millimetres (12.0 in).The cone is placed on a hard non-absorbent surface.
Superplasticizers (SPs), also known as high range water reducers, are additives used for making high-strength concrete or to place self-compacting concrete. Plasticizers are chemical compounds enabling the production of concrete with approximately 15% less water content. Superplasticizers allow reduction in water content by 30% or more.
During the 1980s, Okamura and his Ph.D. student Kazamasa Ozawa at the University of Tokyo developed self-compacting concrete (SCC) which was cohesive, but flowable and took the shape of the formwork without use of any mechanical compaction. SCC is known as self-consolidating concrete in the United States. SCC is characterized by the following:
Samples of "ground granulated blast furnace slag" (left) and "granulated blast furnace slag" (right) Ground granulated blast-furnace slag (GGBS or GGBFS) is obtained by quenching molten iron slag (a by-product of iron and steel-making) from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder.
Changes of pore water content due to drying or wetting processes cause significant volume changes of concrete in load-free specimens. They are called the shrinkage (typically causing strains between 0.0002 and 0.0005, and in low strength concretes even 0.0012) or swelling (< 0.00005 in normal concretes, < 0.00020 in high strength concretes).
The rebuilt upper reservoir of the Taum Sauk plant, nearing completion in this photo, is the largest RCC dam in North America. [1]Roller-compacted concrete (RCC) or rolled concrete (rollcrete) is a special blend of concrete that has essentially the same ingredients as conventional concrete but in different ratios, and increasingly with partial substitution of fly ash for portland cement. [2]