There are two simple regular lattices that achieve this highest average density. They are called face-centered cubic (FCC) (also called cubic close packed) and hexagonal close-packed (HCP), based on their symmetry. Both are based upon sheets of spheres arranged at the vertices of a triangular tiling; they differ in how the sheets are stacked ...
Face-centered cubic (abbreviated cF or fcc) Note: the term fcc is often used in synonym for the cubic close-packed or ccp structure occurring in metals. However, fcc stands for a face-centered-cubic Bravais lattice, which is not necessarily close-packed when a motif is set onto the lattice points.
The IVM scaffolding or skeletal framework is defined by cubic closest packed spheres (CCP), alternatively known as the FCC or face-centered cubic lattice, or as the octet truss in architecture (on which Fuller held a patent).
The diamond crystal structure belongs to the face-centered cubic lattice, with a repeated two-atom pattern. In crystallography, a crystal system is a set of point groups (a group of geometric symmetries with at least one fixed point). A lattice system is a set of Bravais lattices.
This type of structural arrangement is known as cubic close packing (ccp). The unit cell of a ccp arrangement of atoms is the face-centered cubic (fcc) unit cell. This is not immediately obvious as the closely packed layers are parallel to the {111} planes of the fcc unit cell. There are four different orientations of the close-packed layers.
Octahedral (red) and tetrahedral (blue) interstitial symmetry polyhedra in a face-centered cubic lattice. The actual interstitial atom would ideally be in the middle of one of the polyhedra. A close packed unit cell, both face-centered cubic and hexagonal close packed, can form two different shaped holes.
For a face-centered cubic unit cell, the number of atoms is four. A line can be drawn from the top corner of a cube diagonally to the bottom corner on the same side of the cube, which is equal to 4r. Using geometry, and the side length, a can be related to r as: =.
Slip in face centered cubic (fcc) crystals occurs along the close packed plane. Specifically, the slip plane is of type {111} , and the direction is of type < 1 10>. In the diagram on the right, the specific plane and direction are (111) and [ 1 10], respectively.