2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and a maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
The use of larger gauge stranded aluminum wire (larger than #8 AWG) is fairly common in much of North America for modern residential construction. Aluminum wire is used in residential applications for lower voltage service feeders from the utility to the building. This is installed with materials and methods as specified by the local electrical ...
3004 aluminium alloy is an alloy in the wrought aluminium-manganese alloys family (3000 or 3xxx series). It is similar to the 3003 alloy, except for the addition of approximately 1% magnesium.
2195 aluminium alloy is an alloy in the wrought aluminium-copper family (2000 or 2xxx series). It is one of the Weldalite family of Aluminium–lithium alloys. [1] It is one of the most complex grades in the 2000 series, with at least 91.9% aluminium by weight. 2195 aluminium can be alternately referred to by the UNS designation A92195.
5456 aluminium–magnesium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). While it is closely related to 5356 aluminium alloy (Aluminum Association designations that only differ in the second digit are variations on the same alloy), it is used in structural applications, like most other aluminium-magnesium alloys, and not as filler for welding.
ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes; ASTM B308/308M: Standard Specification for Aluminum-Alloy 6061-T6 Standard Structural Profiles; ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
5154 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. 5154 aluminium is commonly used in welded structures such as pressure vessels and ships.
The retrogression and reage (RRA) temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper, it involves overaging past peak hardness (T6 temper) to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels. [10]