Nominal Pipe Size (NPS) is a North American set of standard sizes for pipes used for high or low pressures and temperatures. [1] " Nominal" refers to pipe in non-specific terms and identifies the diameter of the hole with a non-dimensional number (for example – 2-inch nominal steel pipe" consists of many varieties of steel pipe with the only criterion being a 2.375-inch (60.3 mm) outside ...
Pipe sizes are documented by a number of standards, including API 5L, ANSI/ASME B36.10M (Table 1) in the US, and BS 1600 and BS 1387 in the United Kingdom. Typically the pipe wall thickness is the controlled variable, and the Inside Diameter (I.D.) is allowed to vary. The pipe wall thickness has a variance of approximately 12.5 percent.
Standard dimension ratio (SDR) is a method of rating a pipe's durability against pressure. The standard dimension ratio describes the correlation between the pipe dimension and the thickness of the pipe wall. [1] Common nominations are SDR11, SDR17, SDR26 and SDR35. Pipes with a lower SDR can withstand higher pressures.
While pipe sizes in Australia are inch-based, they are classified by outside rather than inside diameter (e.g., a nominal 3 ⁄ 4 inch copper pipe in Australia has measured diameters of 0.750 inches outside and 0.638 inches inside, whereas a nominal 3 ⁄ 4 inch copper pipe in the U.S. and Canada has measured diameters of 0.875 inch outside and ...
The SMYS is required to determine the maximum allowable operating pressure (MAOP) of a pipeline, as determined by Barlow's Formula which is P = (2 * S * T)/(OD * SF), where P is pressure, OD is the pipe’s outside diameter, S is the SMYS, T is its wall thickness, and SF is a [Safety Factor].
Cast iron pipe formed using this procedure was typically oven-cooled under controlled time and temperature conditions. As with metal molds, pipe was typically annealed to eliminate any stresses in the pipe, and were then cleaned, inspected, tested, gauged (for dimensions), coated internally and/or externally, and stored for use. [5]
The inside diameters under IPS were roughly the same as the more modern Ductile Iron Pipe Standard (DIPS) and Nominal Pipe Size (NPS) Standards, and some of the wall thicknesses were also retained with a different designator. In 1948, the DIPS came into effect, when greater control of a pipe's wall thickness was possible.
For pipelines, this value is derived from Barlow's Formula, which takes into account wall thickness, diameter, allowable stress (which is a function of the material used), and a safety factor. The MAOP is less than the MAWP ( maximum allowable working pressure ).