Brushed finishes also typically have a detrimental effect on corrosion resistance. In particular the brushed texture limits the ability of fluid to bead on the material surface. In the case of stainless steel the grooves of the finish can accumulate chloride ions which break down the chromium oxide passivation layer, enabling rusting to occur.
The dual finishing process uses the best each process has to offer, anodizing with its hard wear resistance and chromate conversion coating with its electrical conductivity. The process steps can typically involve chromate conversion coating the entire component, followed by a masking of the surface in areas where the chromate coating must ...
A #7 finish is produced by polishing with a 280–320 grit belt or wheel and sisal buffing with a cut and color compound. This is a semi-bright finish that will still have some polishing lines but they will be very dull. Carbon steel and iron are commonly polished to a #7 finish before chrome plating.
anodizing – electrolytic passivation process used to increase the thickness of the natural oxide layer, producing a porous surface which can accept organic or inorganic dyes easily. In the case of titanium, niobium, and stainless steel, the colour formed is dependent on the thickness of the oxide (which is determined by the anodizing voltage).
Mill finish is the surface texture (or finish) of metal after it exits a rolling mill, extrusion die, or drawing processes, including sheet, bar, plate, or structural shapes. This texture is usually rough and lacks lustre; it may have spots of oxidation or contamination with mill oil.
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound.
Panel edge staining. Panel edge staining is a naturally occurring problem that occurs to anodized aluminium and stainless steel panelling and façades.It is semi-permanent staining that dulls the panel or façade's surface (in particular the edges of the panelling), reducing the natural lustre and shine produced by the anodizing processes used on the aluminium.
In the aluminum industry, the process is also called chemical film [13] or yellow iridite, [13] Commercial trademarked names include Iridite [13] and Bonderite [14] (formerly known as Alodine, or Alocrom in the UK). [15] The main standards for chromate conversion coating of aluminium are MIL-DTL-5541 in the US, and Def Stan 03/18 in the UK.