Superplasticizers (SPs), also known as high range water reducers, are additives used for making high-strength concrete or to place self-compacting concrete. Plasticizers are chemical compounds enabling the production of concrete with approximately 15% less water content. Superplasticizers allow reduction in water content by 30% or more.
Water reducers offer several advantages in their use, listed below: reduces the water content by 5-10%; decreases the concrete porosity; increases the concrete strength by up to 25% (as less water is required for the concrete mixture to remain workable) increases the workability (assuming the amount of free water remains constant)
These low range water reducing dispersants are commonly manufactured from lignosulfonates, a by-product from the paper industry. High range superplasticizers (dispersants) have generally been manufactured from sulfonated naphthalene condensate, although polycarboxylic ethers represent more modern alternatives. Both of these high range water ...
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
The performance of a concrete mix can be altered by use of admixtures. Admixtures can be used to reduce water requirements, entrain air into a mixture, to improve surface durability, or even superplasticise concrete to make it self-levelling, as self-consolidating concrete, [14] the use of admixtures requires precision in dosing and mix design ...
Global warming potential (GWP) of GGBS decreased by 1.1 kg CO 2 eq/m 3, while FA decreased by 17.3 kg CO 2 eq/m 3 when the mineral admixture replacement ratio was increased by 10%. This study also compared the compressive strength properties of binary blended low-carbon concrete according to the replacement ratios, and the applicable range of ...
The parts are in terms of weight – not volume. For example, 1-cubic-foot (0.028 m 3) of concrete would be made using 22 lb (10.0 kg) cement, 10 lb (4.5 kg) water, 41 lb (19 kg) dry sand, 70 lb (32 kg) dry stone (1/2" to 3/4" stone). This would make 1-cubic-foot (0.028 m 3) of concrete and would weigh about 143 lb (65 kg). The sand should be ...
A cement accelerator is an admixture for the use in concrete, mortar, rendering or screeds. The addition of an accelerator speeds the setting time and thus cure time starts earlier. [ 1 ] This allows concrete to be placed in winter with reduced risk of frost damage. [ 2 ]