2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and a maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
The retrogression and reage (RRA) temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper, it involves overaging past peak hardness (T6 temper) to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels. [10]
6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. [ 2 ]
An overview of the Hot Form Quench process. Hot forming of aluminium alloys consists of four main steps performed on a custom-shaped sheet blank: heating and solutionising (above 450°C), blank transfer, quenching (to near ambient temperature) and forming, and artificial aging.
3003 aluminium alloy is an alloy in the wrought aluminium-manganese family (3000 or 3xxx series). It can be cold worked (but not, unlike some other types of aluminium alloys, heat-treated) to produce tempers with a higher strength but a lower ductility. Like most other aluminium-manganese alloys, 3003 is a general-purpose alloy with moderate ...
1100 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). With a minimum of 99.0% aluminium, it is the most heavily alloyed of the 1000 series. It is also the mechanically strongest alloy in the series, and is the only 1000-series alloy commonly used in rivets.