Electroless nickel-boron coating (often called NiB coating) is a metal plating process that can create a layer of a nickel-boron alloy on the surface of a solid substrate, like metal or plastic. The process involves dipping the substrate in a water solution containing nickel salt and a boron-containing reducing agent , such as an ...
Boriding, also called boronizing, is the process by which boron is added to a metal or alloy.It is a type of surface hardening.In this process boron atoms are diffused into the surface of a metal component.
Electroless nickel-phosphorus coatings with less than 7% phosphorus are solid solutions with a microcrystalline structure, with each grain 2–6 nm across. Coatings with more than 10% phosphorus are amorphous. Between these two limits, the coating is a mixture of amorphous and microcrystalline materials. [16]
Cleanliness is essential to successful electroplating, since molecular layers of oil can prevent adhesion of the coating. ASTM B322 is a standard guide for cleaning metals prior to electroplating. Cleaning includes solvent cleaning, hot alkaline detergent cleaning, electrocleaning, ultrasonic cleaning and acid treatment. The most common ...
Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [ 3 ] To clean and protect the part during the plating process, a combination of heat treating , cleaning, masking, pickling , and etching may be used. [ 1 ]
There are a number of ways of forming boride coatings, including gas boriding, molten salt boriding, and pack boriding. [6] Typically carbon tetraboride (B 4 C) or crystalline boron, is sintered on the iron surface in a tetrafluoroborate flux to form the coatings. The boron atoms diffuse into the iron substrate between 1023 and 1373 K.
In physical chemistry and engineering, passivation is coating a material so that it becomes "passive", that is, less readily affected or corroded by the environment. . Passivation involves creation of an outer layer of shield material that is applied as a microcoating, created by chemical reaction with the base material, or allowed to build by spontaneous oxidation
electroplating – coating the metal surface with another metal using electrolysis. patination – chemically reacting the metal surface to form a colored oxide or salt. [1] anodizing – electrolytic passivation process used to increase the thickness of the natural oxide layer, producing a porous surface which can accept organic or inorganic ...