Slow strain rate testing (SSRT), also called constant extension rate tensile testing (CERT), is a popular test used by research scientists to study stress corrosion cracking. It involves a slow (compared to conventional tensile tests) dynamic strain applied at a constant extension rate in the environment of interest.
The sole purpose of the salt spray test is to compare and contrast results with previous experience to perform a quality audit. So, for example, a spray test can be used to ‘police’ a production process and forewarn of potential manufacturing problems or defects, which might affect corrosion resistance. [1]
Both the legacy NACE and SSPC organizations were ANSI-accredited standards developers, which AMPP plans to continue.The merged standards program includes 25 standing standards committees that develop technical standards for industries including cathodic protection, coatings, defense, highways and bridges, rail, maritime, oil and gas, power and utilities, research and testing, tanks and ...
The American Society for Nondestructive Testing, Inc. or ASNT is a technical society for nondestructive testing (NDT) professionals. ASNT evolved from The American Industrial Radium and X-ray Society which was founded in 1941. [1]
Stress-Corrosion-Cracking-Quench-Pipe-1.4541-01. Stress corrosion cracking (SCC) is the growth of a crack in a corrosive environment. [53] It requires three conditions to take place: 1)corrosive environment 2)stress 3)susceptible material. SCC can lead to unexpected sudden and hence catastrophic failure of normally ductile metals under tensile ...
Pitting resistance equivalent number (PREN) is a predictive measurement of a stainless steel's resistance to localized pitting corrosion based on its chemical composition. In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride.
DCVG (direct current voltage gradient) is a survey technique used for assessing the effectiveness of corrosion protection on buried steel structures. [1] In particular, oil and natural gas pipelines are routinely monitored using this technique to help locate coating faults and highlight deficiencies in their cathodic protection (CP) strategies.
ASTM F519 is the Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments. There are 7 different samples designs and the two most commons tests are (1) the rapid test, the Rising step load testing (RSL) method per ASTM F1624 and (2) the sustained load test, which takes 200 hours ...