A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
Vickers hardness test; Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ...
The term "macroindentation" is applied to tests with a larger test load, such as 1 kgf or more. There are various macroindentation tests, including: Vickers hardness test (HV), which has one of the widest scales. Widely used to test hardness of all kinds of metal materials (steel, nonferrous metals, tinsel, cemented carbide, sheet metal, etc ...
Whereas the Vickers scale is widely accepted as a most common test, [11] there remain controversies on the weight load to be applied during the test. This is because Vickers hardness values are load-dependent. An indent made with 0.5N will indicate a higher hardness value than an indent made with 50N.
where HV is the Vickers hardness in N/mm 2 (or MPa) (i.e., 9.81 x numerical HV), P is the indentation load in N (typically 30 kgf is used) and T is the total crack length (mm) after application of the indenter.
Scratch hardness. The Mohs scale of mineral hardness; The Vickers hardness test; The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale; The Rosiwal scale; The Meyer hardness test; The Knoop hardness test
Indentation hardness measures the resistance of a sample to material deformation due to a constant compression load from a sharp object. Tests for indentation hardness are primarily used in engineering and metallurgy. The tests work on the basic premise of measuring the critical dimensions of an indentation left by a specifically dimensioned ...