The chemical compositions of the solid and liquid metals affect the severity of embrittlement. The addition of third elements to the liquid metal may increase or decrease the embrittlement and alter the temperature region over which embrittlement is seen. Metal combinations which form intermetallic compounds do not cause LME.
Metal-induced embrittlement (MIE) is the embrittlement caused by diffusion of metal, either solid or liquid, into the base material. Metal induced embrittlement occurs when metals are in contact with low-melting point metals while under tensile stress. The embrittler can be either solid or liquid (liquid metal embrittlement).
Adsorption embrittlement is the embrittlement caused by wetting. Liquid metal embrittlement (LME) is the embrittlement caused by liquid metals. Metal-induced embrittlement (MIE) is the embrittlement caused by diffusion of atoms of metal, either solid or liquid, into the material. For example, cadmium coating on high-strength steel, which was ...
Induction heating is a non contact heating process which uses the principle of electromagnetic induction to produce heat inside the surface layer of a work-piece. By placing a conductive material into a strong alternating magnetic field, electric current can be made to flow in the material thereby creating heat due to the I 2 R losses in the material.
Fatigue has traditionally been associated with the failure of metal components which led to the term metal fatigue. In the nineteenth century, the sudden failing of metal railway axles was thought to be caused by the metal crystallising because of the brittle appearance of the fracture surface, but this has since been disproved. [ 1 ]
Calculated metastable miscibility gap in the Fe-Cr binary system (remake of [16] [17]) [1]. Duplex stainless steel can have limited toughness due to its large ferritic grain size, and its tendencies to hardening and embrittlement, i.e., loss of plasticity, at temperatures ranging from 250 to 550 °C (482 to 1,022 °F), especially at 475 °C (887 °F). [18]
The average price for low-grade gallium was $120 per kilogram in 2016 and $135–140 per kilogram in 2017. [69] In 2017, the world's production of low-grade gallium was c. 315 tons—an increase of 15% from 2016. China, Japan, South Korea, Russia, and Ukraine were the leading producers, while Germany ceased primary production of gallium in 2016.
In fracture mechanics, intergranular fracture, intergranular cracking or intergranular embrittlement occurs when a crack propagates along the grain boundaries of a material, usually when these grain boundaries are weakened. [1] The more commonly seen transgranular fracture occurs when the crack grows through the material grains. As an analogy ...