4301-304-00-I and X5CrNi18-9, the ISO 15510 name and designation. UNS S30400 in the unified numbering system. A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent ...
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.
It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa ⋅ m 3 / kg , or N ⋅m/kg, which is dimensionally equivalent to m 2 /s 2 , though the latter form is rarely used.
Sulfuric acid is one of the most-produced industrial chemicals. At room temperature, type 304 stainless steel is only resistant to 3% acid, while type 316 is resistant to 3% acid up to 50 °C (120 °F) and 20% acid at room temperature. Thus type 304 SS is rarely used in contact with sulfuric acid.
SAE 316 stainless steel is a molybdenum-alloyed steel and the second most common austenitic stainless steel (after grade 304). It is the preferred steel for use in marine environments because of its greater resistance to pitting corrosion than most other grades of steel without molybdenum. [1] The fact that it is negligibly responsive to ...
Type 308—used as the filler metal when welding 304. Type 309—better temperature resistance than 304, also sometimes used as filler metal when welding dissimilar steels, along with inconel. Type 310 310S— is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the ...
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
Martensitic stainless steels can be high- or low-carbon steels built around the composition of iron, 12% up to 17% chromium, carbon from 0.10% (Type 410) up to 1.2% (Type 440C): [8] The chromium and carbon contents are balanced to have a martensitic structure.