Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Typical material properties for 6060 aluminum alloy include: [2] Density: 2.710 g/cm 3, or 169 lb/ft 3. Young's modulus: 70 GPa, or 10 Msi, or 303 EMEC; Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate; ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes; ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
Typical material properties for 6005 aluminium alloy include: [2] Density: 2.70 g/cm 3, or 169 lb/ft 3. Young's modulus: 69 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Expansion: 23 μm/m-K.
Many standardised alloys have a silicon surplus. It has little influence on the solubility of magnesium silicide, increases the strength of the material more than an Mg excess or an increase in the Mg 2 Si content, increases the volume and the number of excretions and accelerates excretion during cold and hot curing. It also binds unwanted ...
6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards (from any mixture of ASTM, EN, ISO, and national standard bodies), 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.