The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
The hardness of a material can be measured in many ways. The Knoop hardness test, a method of microindentation hardness, is the most reproducible for dense ceramics. The Vickers hardness test and superficial Rockwell scales (e.g., 45N) can also be used, but tend to cause more surface damage than Knoop. The Brinell test is suitable for ductile ...
Vickers hardness test; Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ...
The Mohs scale of mineral hardness; The Vickers hardness test; ... Hardness scales may also refer to: Methods of measuring the deposit formation by hard water.
Hardness Testing. Vickers hardness test (HV), which has one of the widest scales; Brinell hardness test (HB) Knoop hardness test (HK), for measurement over small areas; Janka hardness test, for wood; Meyer hardness test; Rockwell hardness test (HR), principally used in the USA; Shore durometer hardness, used for polymers; Barcol hardness test ...
ISO 409 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces ISO 409-1:1982 Metallic materials — Hardness test — Tables of Vickers hardness values for use in tests made on flat surfaces — Part 1: HV 5 to HV 100 [Withdrawn: replaced with ISO 6507-1 and ISO 6507-4]
Whereas the Vickers scale is widely accepted as a most common test, [11] there remain controversies on the weight load to be applied during the test. This is because Vickers hardness values are load-dependent. An indent made with 0.5N will indicate a higher hardness value than an indent made with 50N.