When a reinforced concrete member is put in tension, after cracking, the member elongates by widening of cracks and by formation of new cracks. Figure 1 Formation of internal cracks. Ignoring the small elastic strain in the concrete between the cracks, we can relate the crack width to the strain of the member by:
Concrete has a very low coefficient of thermal expansion, and as it matures concrete shrinks. All concrete structures will crack to some extent, due to shrinkage and tension. Concrete which is subjected to long-duration forces is prone to creep. The density of concrete varies, but is around 2,400 kilograms per cubic metre (150 lb/cu ft). [1]
Concrete creep is essentially the sagging of concrete over time. Creep and shrinkage of concrete are two physical properties of concrete.The creep of concrete, which originates from the calcium silicate hydrates (C-S-H) in the hardened Portland cement paste (which is the binder of mineral aggregates), is fundamentally different from the creep of metals and polymers.
The steel shuttering pinches the top surface of a concrete slab due to the weight of the next slab being constructed. Concrete slabs, block walls and pipelines are susceptible to cracking during ground settlement, seismic tremors or other sources of vibration, and also from expansion and contraction during adverse temperature changes.
A concrete slab is a common structural element of modern buildings, consisting of a flat, horizontal surface made of cast concrete. Steel- reinforced slabs, typically between 100 and 500 mm thick, are most often used to construct floors and ceilings, while thinner mud slabs may be used for exterior paving ( see below ).
Frost damage can occur as cracks, stone splinters and swelling of the material. When water freezes, the volume of water increases by 9 %. [citation needed] When the volumetric moisture content exceeds 91 %, then the volume increase of water in the pores of the material caused by freezing cannot be absorbed by sufficient empty pores. This causes ...
A fairly well-defined reaction front can often be observed in thin sections; ahead of the front the concrete is normal, or near normal. Behind the reaction front, the composition and the microstructure of concrete are modified. These changes may vary in type or severity but commonly include: Extensive cracking; Expansion
Concrete fracture analysis is part of fracture mechanics that studies crack propagation and related failure modes in concrete. [17] As it is widely used in construction, fracture analysis and modes of reinforcement are an important part of the study of concrete, and different concretes are characterized in part by their fracture properties. [ 18 ]