AlSi10Mg is a lightweight, high-strength aluminium alloy that is widely used in the aerospace, automotive, and medical industries. Its unique combination of aluminium , silicon , and magnesium makes it an ideal material for additive manufacturing processes, such as 3D printing .
The AlMgSi alloys are therefore understood in the standards as a separate group (6000 series) and not as a subgroup of aluminum-magnesium alloys that cannot be hardenable. AlMgSi is one of the aluminum alloys with medium to high strength, high fracture resistance, good welding suitability, corrosion resistance and formability. They can be ...
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.
0–9. 1050 aluminium alloy; 1060 aluminium alloy; 1070 aluminium alloy; 1100 aluminium alloy; 1145 aluminium alloy; 1199 aluminium alloy; 1200 aluminium alloy
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards (from any mixture of ASTM, EN, ISO, and national standard bodies), 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy ...
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
This occurs in dragon eggs, where slower oxidation of magnesium by Lead tetraoxide (Pb 3 O 4) allows time for the formed Lead monoxide (PbO) gas to build up without reacting with the aluminum portion, so when the magnesium is finally consumed the aluminum reaction occurs rapidly enough to produce an explosion. If too much magnesium is present ...