Abrams' law (also called Abrams' water-cement ratio law) [1] is a concept in civil engineering. The law states the strength of a concrete mix is inversely related to the mass ratio of water to cement. [1] [2] As the water content increases, the strength of concrete decreases. Abrams’ law is a special case of a general rule formulated ...
Water content or moisture content is the quantity of water contained in a material, such as soil (called soil moisture), rock, ceramics, crops, or wood. Water content is used in a wide range of scientific and technical areas, and is expressed as a ratio, which can range from 0 (completely dry) to the value of the materials' porosity at saturation.
Saturated unit weight The unit weight of a soil when all void spaces of the soil are completely filled with water, with no air. The formula for saturated unit weight is: = (+) + where γ s is the saturated unit weight of the material; γ w is the unit weight of water; G s is the specific gravity of the solid; e is the void ratio [3] Submerged ...
Changes of pore water content due to drying or wetting processes cause significant volume changes of concrete in load-free specimens. They are called the shrinkage (typically causing strains between 0.0002 and 0.0005, and in low strength concretes even 0.0012) or swelling (< 0.00005 in normal concretes, < 0.00020 in high strength concretes).
Flow table with a grip and a hinge, 70 centimetres (28 in) square. In the American version of this test, the table is 10 inches (25 cm) diameter per ASTM C 230.; Abrams cone, open at the top and at the bottom - 30 centimetres (12 in) high, 17 centimetres (6.7 in) top diameter, 25 centimetres (9.8 in) base diameter.
The test hammer hits the concrete at a defined energy. Its rebound is dependent on the hardness of the concrete and is measured by the test equipment. By reference to a conversion chart, the rebound value can be used to determine the concrete's compressive strength. When conducting the test, the hammer should be held at right angles to the ...
The mixture has a water-to-cement ratio of 0.28 to 0.40 with a void content of 15 to 25 percent. [8] The correct quantity of water in the concrete is critical. A low water to cement ratio will increase the strength of the concrete, but too little water may cause surface failure. A proper water content gives the mixture a wet-metallic appearance.
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]