The weld is triangular in shape and may have a concave, flat or convex surface depending on the welder's technique. Welders use fillet welds when connecting flanges to pipes and welding cross sections of infrastructure, and when bolts are not strong enough and will wear off easily. [1] There are two main types of fillet weld: transverse fillet ...
Welding joint. In metalworking, a welding joint is a point or edge where two or more pieces of metal or plastic are joined together. They are formed by welding two or more workpieces according to a particular geometry. There are five types of joints referred to by the American Welding Society: butt, corner, edge, lap, and tee. These types may ...
Many welding processes require the use of a particular joint design; for example, resistance spot welding, laser beam welding, and electron beam welding are most frequently performed on lap joints. Other welding methods, like shielded metal arc welding, are extremely versatile and can weld virtually any type of joint.
Porosity occurs when the gases produced by the weld flux insufficiently shield the molten weld metal. An overexposed weld bead absorbs nitrogen, oxygen, and hydrogen from the atmosphere; these gases form tiny voids in the weld bead and are released while the weld cools. Poor fusion also affects the strength of the weld and is often easily visible.
The weld pool must be carried along the joint in a consistent width and depth, and the motion used to carry the weld pool has a direct effect on the quality of the weld bead. A weld made by starting and carrying a weld pool, without the addition of a filler material, is called an autogenous weld.
Trained welders are taught to keep the bead the same size at the beginning of the weld as at the end. If the bead gets too wide, the welder increases the speed of welding travel. If the bead gets too narrow or if the weld puddle is lost, the welder slows down the speed of travel. Welding in the vertical or overhead positions is typically slower ...
Spray transfer GMAW. Gas metal arc welding (GMAW), sometimes referred to by its subtypes metal inert gas (MIG) and metal active gas (MAG) is a welding process in which an electric arc forms between a consumable MIG wire electrode and the workpiece metal(s), which heats the workpiece metal(s), causing them to fuse (melt and join).
Weld mapping is the process of assigning information to a weld repair or joint to enable easy identification of weld processes, production (welders, their qualifications, date welded), quality (visual inspection, NDT, standards and specifications) and traceability (tracking weld joints and welded castings, the origin of weld materials).