Gamma double prime (γ"): This phase typically is Ni 3 Nb or Ni 3 V and is used to strengthen Ni-based superalloys at lower temperatures (<650 °C) relative to γ'. The crystal structure of γ" is body-centered tetragonal (BCT), and the phase precipitates as 60 nm by 10 nm discs with the (001) planes in γ" parallel to the {001} family in γ.
Inconel 939: Gamma prime strengthened to increase weldability; In age hardening or precipitation strengthening varieties, alloying additions of aluminum and titanium combine with nickel to form the intermetallic compound Ni 3 (Ti,Al) or gamma prime (γ′). Gamma prime forms small cubic crystals that inhibit slip and creep effectively at ...
Tetramethyl acetyloctahydronaphthalenes (International Nomenclature for Cosmetic Ingredients name) (1-(1,2,3,4,5,6,7,8-ottaidro-2,3,8,8,-tetrametil-2-naftil)etan-1-one) is a synthetic ketone fragrance also known as OTNE (octahydrotetramethyl acetophenone) and by other commercial trade names such as: Iso E Super, Iso Gamma Super, Anthamber, Amber Fleur, Boisvelone, Iso Ambois, Amberlan, Iso ...
Austenite, also known as gamma-phase iron (γ-Fe), is a metallic, non-magnetic allotrope of iron or a solid solution of iron with an alloying element. [1] In plain-carbon steel , austenite exists above the critical eutectoid temperature of 1000 K (727 °C); other alloys of steel have different eutectoid temperatures.
Alpha and near-alpha alloys The micro-structure of alpha alloys cannot be strongly manipulated by heat treatment since alpha alloys undergo no significant phase change. As a result, high strength can not be acquired for the alpha alloys by heat treatment. Yet, alpha and near-alpha titanium alloys can be stress relieved and annealed. Alpha-beta ...
Bainite is a plate-like microstructure that forms in steels at temperatures of 125–550 °C (depending on alloy content). [1] First described by E. S. Davenport and Edgar Bain, [2] [3] it is one of the products that may form when austenite (the face-centered cubic crystal structure of iron) is cooled past a temperature where it is no longer thermodynamically stable with respect to ferrite ...
The G beta-gamma complex (G βγ) is a tightly bound dimeric protein complex, composed of one G β and one G γ subunit, and is a component of heterotrimeric G proteins. Heterotrimeric G proteins, also called guanine nucleotide-binding proteins, consist of three subunits, called alpha , beta, and gamma subunits , or G α , G β , and G γ .
The glass transition of a liquid to a solid-like state may occur with either cooling or compression. [10] The transition comprises a smooth increase in the viscosity of a material by as much as 17 orders of magnitude within a temperature range of 500 K without any pronounced change in material structure. [11]