Search results
Results from the WOW.Com Content Network
Sodium silicate solutions can also be used as a spin-on adhesive layer to bond glass to glass [21] or a silicon dioxide–covered silicon wafer to one another. [22] Sodium silicate glass-to-glass bonding has the advantage that it is a low-temperature bonding technique, as opposed to fusion bonding. [21]
An aqueous solution of sodium silicate is acidified to produce a gelatinous precipitate that is washed, then dehydrated to produce colorless silica gel. [6] When a visible indication of the moisture content of the silica gel is required, ammonium tetrachlorocobaltate(II) (NH 4) 2 [CoCl 4] or cobalt(II) chloride CoCl 2 is added. [6]
Calcium silicate (CaSiO 3), a commonly used anti-caking agent, added to e.g. table salt, absorbs both water and oil. Anticaking agents are also used in non-food items such as road salt , [ 3 ] fertilisers , [ 4 ] cosmetics , [ 5 ] [ 6 ] and detergents .
Silica nevertheless reacts with many metal and metalloid oxides to form a wide variety of compounds important in the glass and ceramic industries above all, but also have many other uses: for example, sodium silicate is often used in detergents due to its buffering, saponifying, and emulsifying properties. [14]
Sulfuric acid and sodium silicate solutions are added simultaneously with agitation to water. Precipitation is carried out under acidic or basic conditions. The choice of agitation , duration of precipitation, the addition rate of reactants, their temperature and concentration and pH can vary the properties of the resulting silica.
3, which is the main component of commercial sodium silicate solutions. It is an ionic compound consisting of sodium cations Na + and the polymeric metasilicate anions [– SiO 2− 3 –] n. It is a colorless crystalline hygroscopic and deliquescent solid, soluble in water (giving an alkaline solution) but not in alcohols. [1]
The subunits of colloidal silica particles are typically in the range of 1 to 5 nm. Whether or not these subunits are joined depends on the conditions of polymerization. Initial acidification of a water-glass (sodium silicate) solution yields Si(OH) 4. If the pH is reduced below 7 or if salt is added, then the units tend to fuse together in chains.
According to one Chinese patent, treated objects can be then immersed in a hot diluted sodium silicate solution (1-5%,95-100 C,3-10 min.). [37] Hexavalent chromates are carcinogenic and toxic, molybdate-based solutions are now being proposed as a substitute (for example molybdate 30-100g/boric acid 10-18 g/ manganese sulfate 0.5-5 g /1 litre ...