A bronze is an alloy of copper and other metals, most often tin, but also aluminium and silicon. Aluminium bronzes are alloys of copper and aluminium. The content of aluminium ranges mostly between 5% and 11%. Iron, nickel, manganese and silicon are sometimes added.
This is a list of named alloys grouped alphabetically by the metal with the highest percentage. Within these headings, the alloys are also grouped alphabetically. Within these headings, the alloys are also grouped alphabetically.
Bronze is an alloy consisting primarily of copper, commonly with about 12–12.5% tin and often with the addition of other metals (including aluminium, manganese, nickel, or zinc) and sometimes non-metals, such as phosphorus, or metalloids, such as arsenic or silicon.
Tin is most commonly alloyed with copper. Pewter is 85–99% tin, [97] and bearing metal has a high percentage of tin as well. [98] [99] Bronze is mostly copper with 12% tin, while the addition of phosphorus yields phosphor bronze. Bell metal is also a copper–tin alloy, containing 22% tin.
Nordic Gold, composed of 89% copper, 5% aluminium, 5% zinc, and 1% tin, is a more recently developed aluminium-bronze alloy for coinage. It was first used for the Swedish 10-kronor coin in 1991, and became widespread after the introduction of Nordic gold 10, 20 and 50-cent Euro coins in 2002.
This page was last edited on 23 September 2023, at 15:55 (UTC).; Text is available under the Creative Commons Attribution-ShareAlike 4.0 License; additional terms may apply.
A typical European casting alloy contains 94% tin, 1% copper and 5% antimony. A European pewter sheet would contain 92% tin, 2% copper, and 6% antimony. Asian pewter, produced mostly in Malaysia, Singapore, and Thailand, contains a higher percentage of tin, usually 97.5% tin, 1% copper, and 1.5% antimony. This makes the alloy slightly softer. [5]
Tin-silver-copper (Sn-Ag-Cu, also known as SAC), is a lead-free alloy commonly used for electronic solder. It is the main choice for lead-free surface-mount technology (SMT) assembly in the industry, [ 1 ] as it is near eutectic , with adequate thermal fatigue properties, strength, and wettability. [ 2 ]