Calcium hydroxide is modestly soluble in water, as seen for many dihydroxides. Its solubility increases from 0.66 g/L at 100 °C to 1.89 g/L at 0 °C. [8] Its solubility product K sp of 5.02 × 10 −6 at 25 °C, [1] its dissociation in water is large enough that its solutions are basic according to the following dissolution reaction:
Each mole of CO 2 (44 g) reacts with one mole of calcium hydroxide (74 g) and produces one mole of water (18 g). The reaction can be considered as a strong-base-catalysed, water-facilitated reaction. [5] The reaction mechanism of carbon dioxide with soda lime can be decomposed in three elementary steps:
Calcium oxide (formula: Ca O), commonly known as quicklime or burnt lime, is a widely used chemical compound. It is a white, caustic , alkaline , crystalline solid at room temperature . The broadly used term lime connotes calcium-containing inorganic compounds , in which carbonates , oxides , and hydroxides of calcium, silicon , magnesium ...
Pure lime is soluble in water containing carbonic acid, a natural, weak acid which is a solution of carbon dioxide in water and acid rain so it will slowly wash away, but this characteristic also produces autogenous or self-healing process where the dissolved lime can flow into cracks in the material and be redeposited, automatically repairing ...
This reaction can take place at anywhere above 840 °C (1,540 °F), but is generally considered to occur at 900 °C (1,650 °F) (at which temperature the partial pressure of CO 2 is 1 atmosphere), but a temperature around 1,000 °C (1,830 °F) (at which temperature the partial pressure of CO 2 is 3.8 atmospheres [1]) is usually used to make the ...
Calcium carbonate reacts with water that is saturated with carbon dioxide to form the soluble calcium bicarbonate. CaCO 3 (s) + CO 2 (g) + H 2 O(l) → Ca(HCO 3 ) 2 (aq) This reaction is important in the erosion of carbonate rock , forming caverns , and leads to hard water in many regions.
Carbonatation is a slow process that occurs in concrete where lime (CaO, or Ca(OH) 2 ) in the cement reacts with carbon dioxide (CO 2) from the air and forms calcium carbonate. The water in the pores of Portland cement concrete is normally alkaline with a pH in the range of 12.5 to 13.5.
The solubility of calcium carbonate (CaCO 3) is controlled largely by the amount of dissolved carbon dioxide (CO 2) in the water. This is summarized in the reaction: CaCO 3 + H 2 O + CO 2 → Ca 2+ + 2HCO − 3. Increases in temperature or decreases in pressure tend to reduce the amount of dissolved CO 2 and precipitate CaCO 3. Reduction in ...