A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
It is usually defined as the ultimate (breaking) force of the fiber (in gram-force units) divided by the denier. Because denier is a measure of the linear density, the tenacity works out to be not a measure of force per unit area, but rather a quasi-dimensionless measure analogous to specific strength. [ 45 ]
Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel). [6] The Japanese equivalent grade of this material is SUS304.
EN 10027-1 steel grade designation system. European standard steel grade names fall into two categories: [1] Steel specified by purpose of use and mechanical properties. Steel specified by chemical composition. The inclusion of a letter 'G' before the code indicates the steel is specified in the form of a casting.
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
SAE 316 and SAE 316L stainless steel, also referred to as marine grade stainless, is a chromium, nickel, molybdenum alloy of steel that exhibits relatively good strength and corrosion resistance. 316L is the low carbon version of 316 stainless steel. [2] 316L in particular is biocompatible when produced to ASTM F138 / F139. [3]