Mu-metal has several compositions. One such composition is approximately 77% nickel, 16% iron, 5% copper, and 2% chromium or molybdenum. [1] [2]More recently, mu-metal is considered to be ASTM A753 Alloy 4 and is composed of approximately
Permeability is influenced by the spacing between the grains, which form distributed air gap; the less gap, the higher permeability and the less-soft saturation. Due to large difference of densities, even a small amount of binder, weight-wise, can significantly increase the volume and therefore intergrain spacing.
Magnetically hard materials have high coercivity, whereas magnetically soft materials have low coercivity. The overall strength of a magnet is measured by its magnetic moment or, alternatively, its total magnetic flux. The local strength of magnetism in a material is measured by its magnetization.
Different materials have different saturation levels. For example, high permeability iron alloys used in transformers reach magnetic saturation at 1.6–2.2 teslas (T), [4] whereas ferrites saturate at 0.2–0.5 T. [5] Some amorphous alloys saturate at 1.2–1.3 T. [6] Mu-metal saturates at around 0.8 T. [7] [8]
They also have high magnetic permeability. These so-called ceramic magnets are cheap, and are widely used in household products such as refrigerator magnets . The maximum magnetic field B is about 0.35 tesla and the magnetic field strength H is about 30–160 kiloampere turns per meter (400–2000 oersteds ). [ 33 ]
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
Sendust composition is typically 85% iron, 9% silicon and 6% aluminium. The powder is sintered into cores to manufacture inductors. Sendust cores have high magnetic permeability (up to 140 000) [ clarification needed ] , low loss, low coercivity (5 A/m) good temperature stability and saturation flux density up to 1 T [ clarification needed ] .
Air and vacuum have high reluctance, while easily magnetized materials such as soft iron have low reluctance. The concentration of flux in low-reluctance materials forms strong temporary poles and causes mechanical forces that tend to move the materials towards regions of higher flux so it is always an attractive force (pull).