For example, 4% electrical steel has an initial relative permeability (at or near 0 T) of 2,000 and a maximum of 38,000 at T = 1 [5] [6] and different range of values at different percent of Si and manufacturing process, and, indeed, the relative permeability of any material at a sufficiently high field strength trends toward 1 (at magnetic ...
For a magnetic circuit constructed with an air gap or air gaps, the permeability of a hypothetical homogeneous material which would provide the same reluctance; (these "effective" above are sizes of a toroid core made from the same material which has the same magnetic properties as the core); Minimum cross-section, A min; Inductance factor, A L
where μ 0 is the vacuum permeability (see table of physical constants), and (1 + χ v) is the relative permeability of the material. Thus the volume magnetic susceptibility χ v and the magnetic permeability μ are related by the following formula: = (+).
Highly magnetic materials have a reduced skin depth owing to their large permeability as was pointed out above for the case of iron, despite its poorer conductivity. A practical consequence is seen by users of induction cookers , where some types of stainless steel cookware are unusable because they are not ferromagnetic.
The permeability of ferromagnetic materials is not constant, but depends on H. In saturable materials the relative permeability increases with H to a maximum, then as it approaches saturation inverts and decreases toward one. [2] [3] Different materials have different saturation levels.
Ferromagnetic materials are noticeably attracted to a magnet, which is a consequence of their substantial magnetic permeability. Magnetic permeability describes the induced magnetization of a material due to the presence of an external magnetic field. For example, this temporary magnetization inside a steel plate accounts for the plate's ...
The typical relative permeability (μ r) of electrical steel is 4,000-38,000 times that of vacuum, compared to 1.003-1800 for stainless steel. [ 15 ] [ 16 ] [ 17 ] The magnetic properties of electrical steel are dependent on heat treatment , as increasing the average crystal size decreases the hysteresis loss.
and permeability is defined as above in § Speed of electromagnetic waves in good dielectrics = the permeability of free space = 4π x 10 −7 H/m. = relative magnetic permeability of the material. Nonmagnetic conductive materials such as copper typically have a near 1.