Compaction of ceramic powders is a forming technique for ceramics in which granular ceramic materials are made cohesive through mechanical densification, either by hot or cold pressing. The resulting green part must later be sintered in a kiln. The compaction process permits an efficient production of parts to close tolerances with low drying ...
In both types of extrusion the raw material must be plasticized to allow and induce the flow of the material in the process. Complex technical ceramic parts are commonly formed using either the injection moulding process or "hot wax moulding." Both rely on heat sensitive plasticizers to allow material flow into a die.
Historically, liquid phase sintering was used to process ceramic materials like clay bricks, earthenware, and porcelain.Modern liquid phase sintering was first applied in the 1930s to materials like cemented carbides (e.g. WC-Co) for cutting tools, porous brass (Cu-Sn) for oil-less bearings, and tungsten-heavy alloys (W-Ni-Cu), but now finds applications ranging from superalloys to dental ...
Liquid phase sintering is the process of adding an additive to the powder which will melt before the matrix phase. The process of liquid phase sintering has three stages: rearrangement – As the liquid melts capillary action will pull the liquid into pores and also cause grains to rearrange into a more favorable packing arrangement.
Freeze-cast alumina that has been partially sintered. The freezing direction in the image is up. Freeze-casting, also frequently referred to as ice-templating, freeze casting, or freeze alignment, is a technique that exploits the highly anisotropic solidification behavior of a solvent (generally water) in a well-dispersed solution or slurry to controllably template directionally porous ...
Simulation of the outside of the Space Shuttle as it heats up to over 1,500 °C (2,730 °F) during re-entry into the Earth's atmosphere Bearing components made from 100% silicon nitride Si 3 N 4 Ceramic bread knife. Ceramic engineering is the science and technology of creating objects from inorganic, non-metallic materials. This is done either ...