HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
Charge carrier density, also known as carrier concentration, denotes the number of charge carriers per volume. In SI units, it is measured in m −3. As with any density, in principle it can depend on position. However, usually carrier concentration is given as a single number, and represents the average carrier density over the whole material.
Typical densities are 29 to 120 kg/m 3 (49 to 202 lb/cu yd) with the lower figure being common. [1] Densities as low as 14 kg/m 3 (24 lb/cu yd) can be produced. [2] Base polymer for EPE foams range from Low-density polyethylene (LDPE) to High-density polyethylene (HDPE). [2]
Young's modulus per density; specific stiffness (10 6 m 2 s −2) Young's modulus per density squared (10 3 m 5 kg −1 s −2) Young's modulus per density cubed (m 8 kg −2 s −2) Reference Latex foam, low density, 10% compression [4] 5.9 × 10 ^ −7: 0.06: 9.83 × 10 ^ −6: 0.000164: 0.00273: Reversible Assembled Cellular Composite ...
ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3). ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M.
For medium- and high-density polyethylene the melting point is typically in the range 120 to 130 °C (248 to 266 °F). The melting point for average commercial low-density polyethylene is typically 105 to 115 °C (221 to 239 °F).
The SI unit for specific strength is Pa⋅m 3 /kg, or N⋅m/kg, which is dimensionally equivalent to m 2 /s 2, though the latter form is rarely used. Specific strength has the same units as specific energy , and is related to the maximum specific energy of rotation that an object can have without flying apart due to centrifugal force .
Mass attenuation coefficients of selected elements for X-ray photons with energies up to 250 keV. The mass attenuation coefficient, or mass narrow beam attenuation coefficient of a material is the attenuation coefficient normalized by the density of the material; that is, the attenuation per unit mass (rather than per unit of distance).