The Hall–Héroult process is the major industrial process for smelting aluminium. It involves dissolving aluminium oxide (alumina) (obtained most often from bauxite , aluminium 's chief ore, through the Bayer process ) in molten cryolite and electrolyzing the molten salt bath, typically in a purpose-built cell.
The process produces a quantity of fluoride waste: perfluorocarbons and hydrogen fluoride as gases, and sodium and aluminium fluorides and unused cryolite as particulates. This can be as small as 0.5 kg per tonne of aluminium in the best plants in 2007, up to 4 kg per tonne of aluminium in older designs in 1974.
The original ingots are usually further processed by other methods (rolling, forging, etc.). More than half of global aluminum production uses the Direct Chill casting process. [1] Direct Chill casting operates by pouring liquid metal continuously into a short mold (7.5–15 cm deep) that is open at the bottom.
The physical structure of a crystalline material is largely determined by the method of cooling and precipitation of the molten metal. During the pouring process, metal in contact with the ingot walls rapidly cools and forms either a columnar structure or possibly a "chill zone" of equiaxed dendrites, depending upon the liquid being cooled and ...
A billet is a length of metal that has a round or square cross-section, with an area less than 36 in 2 (230 cm 2). Billets are created directly via continuous casting or extrusion or indirectly via hot rolling an ingot or bloom. [1] [2] [4] Billets are further processed via profile rolling and drawing. Final products include bar stock and wire. [3]
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots .
Vacuum arc remelting (VAR) is a secondary melting process for production of metal ingots with elevated chemical and mechanical homogeneity for highly demanding applications. [1] The VAR process has revolutionized the specialty traditional metallurgical techniques industry, and has made possible tightly controlled materials used in biomedical ...
A hot top, also known as a feeder head, [5] is a specialized riser, used to help counteract the formation of pipes when casting ingots. It is essentially a live open riser, with a hot ceramic liner instead of just the mold materials. It is inserted into the top of the ingot mould near the end of the pour, and the rest of the metal is then ...