The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F), depending on the alloy in question. This process is mainly suited for low-carbon steel. The material is heated up to a temperature just below the lower critical temperature of steel.
The recrystallization temperature is temperature at which recrystallization can occur for a given material and processing conditions. This is not a set temperature and is dependent upon factors including the following: [3] Increasing annealing time decreases recrystallization temperature
As a result of the transformation, the microconstituents, pearlite and bainite, form; pearlite forms at higher temperatures and bainite at lower. TTT diagram of isothermal transformations of a hypoeutectoid carbon steel; showing the main components obtained when cooling the steel and its relation with the Fe-C phase diagram of carbon steels.
Annealing is the process of heating the steel to a sufficiently high temperature to relieve local internal stresses. It does not create a general softening of the product but only locally relieves strains and stresses locked up within the material. Annealing goes through three phases: recovery, recrystallization, and grain growth. The ...
Steel with a high carbon content will reach a much harder state than steel with a low carbon content. Likewise, tempering high-carbon steel to a certain temperature will produce steel that is considerably harder than low-carbon steel that is tempered at the same temperature. The amount of time held at the tempering temperature also has an effect.
Full annealing A hypoeutectoid carbon steel (carbon composition smaller than the eutectoid one) is heated to approximately 30 to 50 °C (86 to 120 °F) above the austenictic temperature (A 3), whereas a hypereutectoid steel is heated to a temperature above the eutectoid one (A 1) for a certain number of hours; this ensures all the ferrite ...
Production of galvannealed sheet steel begins with hot dip galvanization of sheet steel. After passing through the galvanizing zinc bath the sheet steel passes through air knives to remove excess zinc, and is then heated in an annealing furnace for several seconds causing iron and zinc layers to diffuse into one another causing the formation of zinc-iron alloy layers at the surface.
Annealing is most often used to soften a metal for cold working, to improve machinability, or to enhance properties like electrical conductivity. In ferrous alloys, annealing is usually accomplished by heating the metal beyond the upper critical temperature and then cooling very slowly, resulting in the formation of pearlite. In both pure ...