Learn about the differences between the cement and concrete including what they're used for, what they cost, which is more durable, and what they're made of.
Portland cement blends are often available as inter-ground mixtures from cement producers, but similar formulations are often also mixed from the ground components at the concrete mixing plant. Portland blast-furnace slag cement , or blast furnace cement (ASTM C595 and EN 197-1 nomenclature respectively), contains up to 95% ground granulated ...
Pavers manufactured from concrete go well with flag, brick and concrete walkways or patios. Concrete pavers may be used where winter temperatures dip below freezing. They are available in hole, x-shape, y-shape, pentagon, polygon and fan styles. An interlocking concrete paver, also known as a segmental paver, is a type of paver.
Thinset (also called thinset mortar, thinset cement, dryset mortar, or drybond mortar) is an adhesive mortar made of cement, fine sand and a water-retaining agent such as an alkyl derivative of cellulose. [1] It is usually used to attach tile or stone to surfaces such as cement or concrete. [2]
A cement accelerator is an admixture for the use in concrete, mortar, rendering or screeds. The addition of an accelerator speeds the setting time and thus cure time starts earlier. [ 1 ] This allows concrete to be placed in winter with reduced risk of frost damage. [ 2 ]
Ferrocement or ferro-cement [1] is a system of construction using reinforced mortar [2] or plaster (lime or cement, sand, and water) applied over an "armature" of metal mesh, woven, expanded metal, or metal-fibers, and closely spaced thin steel rods such as rebar. The metal commonly used is iron or some type of steel, and the mesh is made with ...
High-strength concrete has a compressive strength greater than 40 MPa (6000 psi). In the UK, BS EN 206-1 [3] defines High strength concrete as concrete with a compressive strength class higher than C50/60. High-strength concrete is made by lowering the water-cement (W/C) ratio to 0.35 or lower.
A w/c ratio higher than 0.60 is not acceptable as fresh concrete becomes "soup" [2] and leads to a higher porosity and to very poor quality hardened concrete as publicly stated by Prof. Gustave Magnel (1889-1955, Ghent University, Belgium) during an official address to American building contractors at the occasion of one of his visits in the ...