Black oxide or blackening is a conversion coating for ferrous materials, stainless steel, copper and copper based alloys, zinc, powdered metals, and silver solder. [1] It is used to add mild corrosion resistance, for appearance, and to minimize light reflection. [ 2 ]
Black oxide provides minimal protection against corrosion, unless also treated with a water-displacing oil to reduce wetting and galvanic action. In colloquial use, thin coatings of black oxide are often termed "gun bluing", while heavier coatings are termed "black oxide". Both refer to the same chemical process for providing true gun bluing. [1]
Tannic acid chemically converts the reddish iron oxides into bluish-black ferric tannate, a more stable material. [2] The second active ingredient is an organic solvent such as 2-butoxyethanol (ethylene glycol monobutyl ether, trade name butyl cellosolve) that acts as a wetting agent and provides a protective primer layer in conjunction with an ...
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion , to improve the adherence of other coatings, for lubrication , or for aesthetic ...
When coating metric threaded parts it is necessary to keep to the tolerances defined in ISO 965 so that the bolt's thread does not get gummed up and the coefficient of friction can be set accordingly. Hot-dip galvanised fasteners with a typical coating thickness of 80-200 μm have to be grooved again retrospectively in order to expose the thread.
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
A black oxide coating provides heat resistance and lubricity, as well as corrosion resistance. The coating increases the life of high-speed steel bits. Titanium nitride (TiN) is a very hard metallic material that can be used to coat a high-speed steel bit (usually a twist bit), extending the cutting life by three or more times.