For example, tin-lead solder [5] attaches very well to copper metal, but poorly to its oxides, which form quickly at soldering temperatures. By preventing the formation of metal oxides, flux enables the solder to adhere to the clean metal surface, rather than forming beads, as it would on an oxidized surface.
The Kirkendall effect is the motion of the interface between two metals that occurs due to the difference in diffusion rates of the metal atoms. The effect can be observed, for example, by placing insoluble markers at the interface between a pure metal and an alloy containing that metal, and heating to a temperature where atomic diffusion is reasonable for the given timescale; the boundary ...
Wave soldering uses surface tension to keep solder from bridging the insulating gaps between the copper lines of flux-coated printed wiring boards/printed circuit boards. The electric soldering iron is widely used for hand-soldering, consisting of a heating element in contact with the "iron" (a larger mass of metal, usually copper) which is in ...
Solder (UK: / ˈ s ɒ l d ə, ˈ s ə ʊ l d ə /; [1] NA: / ˈ s ɒ d ər /) [2] is a fusible metal alloy used to create a permanent bond between metal workpieces. Solder is melted in order to wet the parts of the joint, where it adheres to and connects the pieces after cooling.
Both quantitative and qualitative tests for solderability exist. [6] The two most common testing methods are the 'dip and look' method and wetting balance analysis.In both of these tests, the soldered pieces undergo an accelerated aging process before being tested for solderability, to take into consideration the time a component was in storage prior to mounting to final assembly.
Soldering copper pipes using a propane torch and a lead-free solder. Solder is a metallic material that is used to connect metal workpieces. The choice of specific solder alloys depends on their melting point, chemical reactivity, mechanical properties, toxicity, and other properties.
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Flux in the wave soldering process has a primary and a secondary objective. The primary objective is to clean the components that are to be soldered, principally any oxide layers that may have formed. [3] There are two types of flux, corrosive and noncorrosive. Noncorrosive flux requires precleaning and is used when low acidity is required.