Gold plated - gold layer thickness greater than or equal to 0.5 micron; Heavy gold plated / Vermeil - gold layer thickness greater than or equal to 2.5 micron; Gold plated silver jewellery can still tarnish as the silver atoms diffuse into the gold layer, causing slow gradual fading of its color and eventually causing tarnishing of the surface ...
Some jewellery is plated to give it a shiny, reflective look or to achieve a desired colour. Sterling silver jewellery may be plated with a thin layer of 0.999 fine silver (a process known as flashing) or plated with rhodium or gold. Base metal costume jewellery may also be plated with silver, gold, or rhodium for a more attractive finish.
In time management, gold plating is the phenomenon of working on a project or task past the point of diminishing returns.. For example, after having met a project's requirements, the manager or the developer works on further enhancing the product, thinking that the customer will be delighted to see additional or more polished features, beyond that which what was asked for or expected.
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...
Electroplating of acid gold on underlying copper- or nickel-plated circuits reduces contact resistance as well as surface hardness. Copper-plated areas of mild steel act as a mask if case-hardening of such areas are not desired. Tin-plated steel is chromium-plated to prevent dulling of the surface due to oxidation of tin.
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
Language links are at the top of the page across from the title.
The Federal Trade Commission allows the use of the terms "rolled gold plate," "R.G.P" or "gold overlay" on items with lower thicknesses of gold than are required for "gold-filled." [ 3 ] An example would be an item stamped as " 1 ⁄ 40 10kt RGP" meaning that the object is plated with 10kt gold at a thickness that makes weight of the plated ...